Structural, magnetic, and blood compatibility studies of Nickel-Copper nanoferrites produced by laser ablation technique
Özçelik, S. ; Özçelik, C. ; Ergin, I. ; Yalçin, B. ; Arda, L. ; Angurel, L. A. (Universidad de Zaragoza) ; de la Fuente, G. F. ; Özçelik, B.
Resumen: This study explores the effects of Cu substitution on the structural, morphological, and magnetic properties of nickel ferrite nanoparticles, Ni1-xCuxFe2O4, where x = 0.25, 0.50, and 0.75. SEM analysis revealed that the particles are spherical with an average size of 7 nm. The Nickel-Copper ferrite nanoparticles presented a characteristic XRD diffraction corresponding to the cubic spinel structure of the Fd3m space group, with no secondary phases formed due to Cu substitution. The crystal sizes of Ni-Cu spinel ferrites were calculated via Debye-Scherrer formula to be between 44.9 and 52 nm. FT-IR results indicated an increase in the force constants of octahedral and tetrahedral bonds with higher Cu content, as evidenced by the main vibration bands. M-H curves displayed S-shaped behavior, suggesting that Cu substitution does not cause drastic changes in magnetic properties. The coercivity field (Hc), saturation magnetization (MS), and remanent magnetization (Mr) values ranged between 13.54 and 6.14 Oe, 48.8–52.7 emu/g, and 0.57–1.14 emu/g, respectively. Blood compatibility experiments showed that the Ni0.25Cu0.75Fe2O4 composition exhibited the highest blood compatibility at low concentrations among the studied samples.
Idioma: Inglés
DOI: 10.1016/j.jallcom.2025.184080
Año: 2025
Publicado en: JOURNAL OF ALLOYS AND COMPOUNDS 1042 (2025), 184080 [8 pp.]
ISSN: 0925-8388
Tipo y forma: Article (Published version)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)
0
Exportado de SIDERAL (2025-10-24-16:55:57)
Idioma: Inglés
DOI: 10.1016/j.jallcom.2025.184080
Año: 2025
Publicado en: JOURNAL OF ALLOYS AND COMPOUNDS 1042 (2025), 184080 [8 pp.]
ISSN: 0925-8388
Tipo y forma: Article (Published version)
Área (Departamento): Área Cienc.Mater. Ingen.Metal. (Dpto. Ciencia Tecnol.Mater.Fl.)
0
Exportado de SIDERAL (2025-10-24-16:55:57)
Este artículo se encuentra en las siguientes colecciones:
articulos > articulos-por-area > ciencia_de_los_materiales_e_ingenieria_metalurgica
Notice créée le 2025-10-24, modifiée le 2025-10-24
Liens externes:
Versión publicada
Versión publicada
Versión publicada
Versión publicada